| Автор | K C Goretta |
| Автор | M E Loomans |
| Автор | L J Martin |
| Автор | J Joo |
| Автор | R B Poeppel |
| Автор | Nan Chen |
| Дата выпуска | 1993-04-01 |
| dc.description | Dense, bulk Bi<sub>2</sub>Sr<sub>2</sub>CaCu<sub>2</sub>O<sub>x</sub> bars were fabricated by sinter forging. The bars exhibited strong textures in which the c axes of the platelike grains were preferentially aligned parallel to the pressing direction. Fracture strength was measured in four-point bending, and in compression at angles of 0, 45, and 90 degrees to the pressing direction. Maximum strength in tension gas 100 MPa and average strength was 84 MPa. Maximum strength in compression, which depended on orientation, was 180 MPa and maximum average strength was 120-135 MPa. |
| Формат | application.pdf |
| Издатель | Institute of Physics Publishing |
| Название | Fracture of dense, textured Bi<sub>2</sub>Sr<sub>2</sub>CaCu<sub>2</sub>O<sub>x</sub> |
| Тип | paper |
| DOI | 10.1088/0953-2048/6/4/012 |
| Electronic ISSN | 1361-6668 |
| Print ISSN | 0953-2048 |
| Журнал | Superconductor Science and Technology |
| Том | 6 |
| Первая страница | 282 |
| Последняя страница | 286 |
| Аффилиация | K C Goretta; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Аффилиация | M E Loomans; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Аффилиация | L J Martin; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Аффилиация | J Joo; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Аффилиация | R B Poeppel; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Аффилиация | Nan Chen; Mater. & Components Technol. Div., Argonne Nat. Lab., IL, USA |
| Выпуск | 4 |