| Автор | Yoshihiko Takano |
| Автор | Takeshi Hatano |
| Автор | Akihiro Fukuyo |
| Автор | Akira Ishii |
| Автор | Shunichi Arisawa |
| Автор | Masashi Tachiki |
| Автор | Kazumasa Togano |
| Дата выпуска | 2001-09-01 |
| dc.description | A Bi<sub>2</sub>Sr<sub>2</sub>CaCu<sub>2</sub>O<sub>8+δ</sub> cross-whiskers junction has been successfully discovered as a novel intrinsic Josephson junction without using any technique for micro-fabrication. Two Bi<sub>2</sub>Sr<sub>2</sub>CaCu<sub>2</sub>O<sub>8+δ</sub> whisker crystals were placed crosswise on a MgO substrate and heated at 850 °C for 30 min. They were electrically connected at their c-planes. The measurement terminals were made at the four ends of the whiskers. The I-V characteristics of the cross-whiskers junction at 5 K were found to show a clear multiple-branch structure with a spacing of approximately 15 mV, which is a feature of an intrinsic Josephson junction. The critical current density J<sub>C</sub> was estimated to be 1170 A cm<sup>-2</sup>. The branch structure was strongly suppressed by a magnetic field above 1 kOe. |
| Формат | application.pdf |
| Издатель | Institute of Physics Publishing |
| Название | A cross-whiskers junction as a novel fabrication process for intrinsic Josephson junctions |
| Тип | paper |
| DOI | 10.1088/0953-2048/14/9/327 |
| Electronic ISSN | 1361-6668 |
| Print ISSN | 0953-2048 |
| Журнал | Superconductor Science and Technology |
| Том | 14 |
| Первая страница | 765 |
| Последняя страница | 769 |
| Выпуск | 9 |