| Автор | Misu, Takeshi |
| Автор | Sakamoto, Naonori |
| Автор | Shinozaki, Kazuo |
| Автор | Adachi, Nobuyasu |
| Автор | Suzuki, Hisao |
| Автор | Wakiya, Naoki |
| Дата выпуска | 2011-06-01 |
| dc.description | Thin films composed of MgAl<sub>2</sub>O<sub>4</sub> and (Ni<sub>0.5</sub>Zn<sub>0.5</sub>)Fe<sub>2</sub>O<sub>4</sub> ([MA(100-x)-NZFx] films) were grown on fused SiO<sub>2</sub> substrates by pulsed laser deposition. X-ray diffraction measurements revealed that the films were polycrystalline, and that their lattice constant varied linearly with composition, indicating the formation of a solid solution. The film with x=60 was paramagnetic and those with x ≥ 70 were ferromagnetic. The films had a transparency above 75% in the visible range, but the transparency decreased with the x value. The optical band gaps were 2.95, 2.55, 2.30 and 1.89 eV for x=20, 40, 60, 80 and 100, respectively. The Faraday rotation angle increased with x in the visible range, and the film with x=70 exhibited a value of 2000 degrees cm<sup>-1</sup> at 570 nm, which is comparable to the rotation angle of Y<sub>3</sub>Fe<sub>5</sub>O<sub>12</sub>. Owing to their high transparency, which extends into the visible range, the [MA(100-x)-NZFx] films can be used in novel magneto-optical devices. |
| Формат | application.pdf |
| Издатель | Institute of Physics Publishing |
| Копирайт | 2011 National Institute for Materials Science |
| Название | Magnetic and optical properties of MgAl<sub>2</sub>O<sub>4</sub>-(Ni<sub>0.5</sub>Zn<sub>0.5</sub>)Fe<sub>2</sub>O<sub>4</sub> thin films prepared by pulsed laser deposition |
| Тип | paper |
| DOI | 10.1088/1468-6996/12/3/034408 |
| Electronic ISSN | 1878-5514 |
| Print ISSN | 1468-6996 |
| Журнал | Science and Technology of Advanced Materials |
| Том | 12 |
| Первая страница | 34408 |
| Последняя страница | 34411 |
| Аффилиация | Misu, Takeshi; Department of Materials Science and Chemical Engineering, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu, Shizuoka 432-8561, Japan |
| Аффилиация | Sakamoto, Naonori; Department of Materials Science and Chemical Engineering, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu, Shizuoka 432-8561, Japan |
| Аффилиация | Shinozaki, Kazuo; Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, 2-12-1 O-okayama, Meguro-ku, Tokyo 152-8550, Japan |
| Аффилиация | Adachi, Nobuyasu; Ceramics Research Laboratory, 10-6-29, Asahigaoka, Tajimi, Gifu 507-0071, Japan |
| Аффилиация | Suzuki, Hisao; Graduate School of Materials Science and Technology, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu, Shizuoka 432-8561, Japan |
| Аффилиация | Wakiya, Naoki; Department of Materials Science and Chemical Engineering, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu, Shizuoka 432-8561, Japan |
| Выпуск | 3 |