Directionally solidified (DS) alloys of the eutectic systems NiAl-10Mo and NiAl-34Cr (at.%) are potential candidates for high-temperature structural applications. Here, these alloys were first arc-melted and drop-cast. Thereafter, they were directionally solidified (DS) at growth rates of 20 and 80 mm/h while rotating at a fixed rotation speed of 60 revolutions per minute. Specimens of the DS alloys were tested in three-point-bending and uniaxial compression to obtain mechanical properties, including the ductile to brittle transition temperature (DBTT). For the NiAl-Cr system DBTT was found to be around 300 °C. Microstructural observations revealed that in the section perpendicular to the growth direction a uniform distribution of fibres was observed. The expected decrease of the fibre diameter with increasing growth rate was not observed. Instead, the fibre diameter slightly increased with increasing crystal growth rates. First compression tests were performed to get insights into the creep behaviour of these fibre-reinforced microstructures.