Mesoporous thiol-functionalized SBA-15 has been directly synthesized by co-condensation of tetraethyl orthosilicate (TEOS) and 3-mercaptopropyltrimethoxysilane (MPTMS) with triblock copolymer P123 as-structure-directing agent under hydrothermal conditions. Surfactant removal was performed by Soxhlet ethanol extraction. These materials have been characterized by powder x-ray diffraction (XRD), nitrogen adsorption/desorption (BET model), transmission electron microscopy (TEM), thermal analysis, infrared spectroscopy (IR) and energy-dispersive x-ray spectroscopy (EDX). The main parameters, such as the initial molar ratio of MPTMS to TEOS, the time of adding MPTMS to synthesized gel and the Soxhlet ethanol extraction on the thiol functionalized SBA-15 with high thiol content and highly ordered hexagonal mesostructure, were investigated and evaluated. The adsorption capacity of the thiol-functionalized and non-functionalized SBA-15 materials for Pb²⁺ ion from aqueous solution was tested. It was found that the Pb²⁺ adsorption capacity of the thiol functionalized SBA-15 is three times higher than that of non-functionalized SBA-15.