| dc.description | Rapidly solidified Al–12.5 Si–1 Ni ribbons were prepared by melt spinning. The Si solid solubility was extended to high values as deduced from X-ray diffraction and TEM. This high solubility of Si was found to have significant effects on the various properties of this alloy. High values of electric resistivity was observed which was about four times the fully annealed values. Furthermore rapid solidification improved the tensile strength and the toughness of this alloy as compared with its classically solidified counter part. The relaxation kinetics was followed by isothermal resistivity measurements. The relaxation follows an equation which has the Johnson-Mehl-Avrami (JMA) form. No metastable phase was observed. |
| Формат | application.pdf |
| Издатель | EDP Sciences |
| Копирайт | © EDP Sciences, 1998 |
| Название | Properties of rapidly solidified Al–12.5 Si–1Ni alloy |
| Тип | research-article |
| DOI | 10.1051/epjap:1998250 |
| Electronic ISSN | 1286-0050 |
| Print ISSN | 1286-0042 |
| Журнал | The European Physical Journal Applied Physics |
| Том | 4 |
| Первая страница | 117 |
| Последняя страница | 124 |
| Аффилиация | Tawfik N. L.; Solid State Physics Department, National Research Centre, Dokki, Giza, Egypt |
| Аффилиация | Abdel Hady E. M.; Solid State Physics Department, National Research Centre, Dokki, Giza, Egypt |
| Аффилиация | Bastawros A. M.; Solid State Physics Department, National Research Centre, Dokki, Giza, Egypt |
| Выпуск | 2 |