Capacité de transport et de limitation du courant des matériaux YBaCuO texturés*
Porcar, L.; Bourgault, D.; Belmont, O.; Noudem, J. G.; Barbut, J. M.; Barrault, M.; Tixador, P.; Chaud, X.; Tournier, R.; Porcar L.; Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France; Bourgault D.; CNRS-EPM/Matformag, B.P. 166, 38042 Grenoble Cedex 09, France; Belmont O.; Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France; Noudem J. G.; Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France; Barbut J. M.; Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France; Barrault M.; Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France; Tixador P.; CNRS-CRTBT/LEG, B.P. 166, 38042 Grenoble Cedex 09, France; Chaud X.; CNRS-EPM/Matformag, B.P. 166, 38042 Grenoble Cedex 09, France; Tournier R.; CNRS-EPM/Matformag, B.P. 166, 38042 Grenoble Cedex 09, France
Журнал:
The European Physical Journal Applied Physics
Дата:
1998
Аннотация:
Afin de déterminer la capacité à limiter le courant du composé ${\rm Y}_1{\rm Ba}_2{\rm Cu}_3{\rm O}_{7-\delta}$ texturé, des études en courants de transport élevés, en régime pulsé et en régime permanent alternatif, ont été menées. Il en résulte que YBaCuO possède une forte capacité de transport du courant en régime pulsé (9000 A soit 23 000 $\ {\rm A} / {\rm cm}^2$ dans un barreau de 4 cm de long) et en régime permanent alternatif (3000 A soit 7800 $\ {\rm A} / {\rm cm}^2$) et que le retour à l'état normal par dépassement du courant critique est très abrupt.
216.8Кб