| Автор | Hoshino, K. |
| Автор | Averback, R. S. |
| Автор | Hahn, H. |
| Автор | Rothman, S. J. |
| Дата выпуска | 1988 |
| dc.description | Tracer diffusion of <sup>60</sup>Co and <sup>63</sup>Ni in the amorphous alloy NiZr near the equiatomic composition has been measured in the temperature range between 486 and 641 K using the ion-beam sputter-sectioning technique for serial sectioning. The temperature dependence for the diffusivities of Co and Ni in a-NiZr exhibit Arrhenius behavior; these can be expressed as follows: D<sup>∗</sup><sub>co</sub> = 3.6 × 10<sup>−7</sup> exp [− (135 ± 14) kJ mol<sup>−1</sup> /RT] m<sup>2</sup>/s and D<sup>∗</sup><sub>Ni</sub> = 1.7 × 10<sup>−7</sup> exp [− (140 ± 9) kJ mol<sup>−1</sup> /RT] m<sup>2</sup>/s. The values of D<sup>∗</sup><sub>Ni</sub> are in good agreement with those measured by the Rutherford backscattering technique. The measured diffusivities were independent of time, indicating that no relaxation took place during diffusion. |
| Формат | application.pdf |
| Издатель | Cambridge University Press |
| Копирайт | Copyright © Materials Research Society 1988 |
| Название | Tracer diffusion of <sup>60</sup>Co and <sup>63</sup>Ni in amorphous NiZr alloy |
| Тип | research-article |
| DOI | 10.1557/JMR.1988.0055 |
| Electronic ISSN | 2044-5326 |
| Print ISSN | 0884-2914 |
| Журнал | Journal of Materials Research |
| Том | 3 |
| Первая страница | 55 |
| Последняя страница | 58 |
| Аффилиация | Hoshino K.; Department of Materials Science and Engineering and Materials Research Laboratory, University of Illinois at Urbana–Champaign, Illinois 61801 |
| Аффилиация | Averback R. S.; Department of Materials Science and Engineering and Materials Research Laboratory, University of Illinois at Urbana–Champaign, Illinois 61801 |
| Аффилиация | Hahn H.; Materials Science Division, Argonne National Laboratory, Argonne, Illinois 60439 |
| Аффилиация | Rothman S. J.; Materials Science Division, Argonne National Laboratory, Argonne, Illinois 60439 |
| Выпуск | 1 |